Industrial Low Cement Refractory Castable For High Temperature Furnace
| MOQ: | 1 Ton |
| Price: | Negotiable |
| Standard Packaging: | Kraft paper bag + Pallet |
| Delivery Period: | 10-15 days |
| Payment Method: | L/C,D/P,T/T,Western Union |
| Supply Capacity: | 2000 tons/month |
Detail Information
Place of Origin
China
Brand Name
LEADSUN
Certification
ISO
Model Number
Low Cement Castable
Usage:
Fire Resistance Place,Furnace Liner,Used In Severe Environment And Conditions,Wear-resisting Material,Industrial Furnace
Refractoriness:
1350-1850C
Size:
1-6mm
Package:
Bag+ Pallet
Al2O3:
40-90%
Color:
Grey
Type:
Low Cement, High Alumina, Insulation Type,plastic,gunning Type
Highlight:
Industrial Low Cement Refractory Castable
,Furnace Low Cement Refractory Castable
Product Description
Low Cement Refractory Castable for high-temperature furnace
Low Cement Castable is formulated with a low content of calcium aluminate cement. It is widely used in applications requiring high refractoriness, excellent corrosion resistance and abrasion resistance.
The castable features a uniform and dense structure with low porosity, providing high strength at both low and intermediate temperatures. The CaO content of Low Cement Castable is usually less than 3%, which ensures excellent mechanical strength and stable performance in the mid-temperature range.
Technical data
| Item | LDSLC75 | LDSLC80 | LDSLC85 | LDSLC95 |
|---|---|---|---|---|
| Service Temp ℃ | 1650 | 1700 | 1750 | 1780 |
| Bulk Density (g/cm3) (Dried at 110℃) |
2.55 | 2.6 | 2.7 | 3.0 |
| CCS 110℃ (Mpa) 1100℃ 1500 ℃ |
65 75 80 |
70 80 85 |
80 90 100 |
90 95 110 |
| MOR 110℃ (Mpa) 1100℃ 1500℃ |
9 10 11 |
10 11 12 |
11 12 13 |
13 14 15 |
| Max Grain Size (mm) | 6 | 6 | 6 | 6 |
| Chemical Analysis(%) Al2O3 CaO Fe2O3 |
75 2-3 2.4 |
80 2-3 2.0 |
85 2-3 1.8 |
95 2-3 1.5 |
| Application Guidelines Mixer Placement Water/Mixer Temp℃ Mixing Time(Min):Dry/Wet |
P V/T 20±5 2/5 |
P V/T 20±5 2/5 |
P V/T 20±5 2/5 |
P V/T 20±5 2/5 |
| Water % (Typical) | 7-9 | 7-9 | 6-8 | 6-7 |
Features
- Low CaO content (≤3%)
- High strength at medium temperatures
- Excellent high-temperature performance
- High wear resistance
Applications
- Cement kilns
- Rotary kilns
- Steelmaking furnaces